PC/日本帝人/L-1250Z100 透明耐候 抗UV稳定 注塑级| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.20 | g/cm3 | |
| 溶化体积流率（MVR） | 300℃/1.2 kg | ISO 1133 | 8.00 | cm3/10min | |
| 收缩率 | 流动 | ASTM D955 | 0.50到 0.70 | % | |
| 横向流动 | ASTM D955 | 0.50 到 0.70 | % | ||
| 横向流量 | ISO 294-4 | 0.50 到 0.70 | % | ||
| 流量 | ISO 294-4 | 0.50到 0.70 | % | ||
| 吸水率 | 23℃, 24 hr | ISO 62 | 0.20 | % | |
| 机械性能 | 洛氏硬度 (M 计秤) | ASTM D785 | 77 | ||
| 拉伸模量 | -- | ASTM D638 | 2120 | MPa | |
| -- | ISO 527-2/1 | 2400 | MPa | ||
| 抗张强度 | 屈服 | ASTM D638 | 62.0 | MPa | |
| 屈服 | ISO 527-2/50 | 61.0 | MPa | ||
| 断裂 | ISO 527-2/5 | 80.0 | MPa | ||
| 伸长率 | 屈服 | ASTM D638 | 6.0 | % | |
| 断裂 | ASTM D638 | 140 | % | ||
| 断张率 | ISO 527-2/50 | 50 | % | ||
| 弯曲模量 | -- | ASTM D790 | 2230 | MPa | |
| -- 3 | ISO 178 | 2350 | MPa | ||
| 弯曲强度 | -- 3 | ISO 178 | 93.0 | MPa | |
| 屈服 | ASTM D790 | 92.0 | MPa | ||
| 压缩强度 | ASTM D695 | 76.0 | MPa | ||
| 简支梁缺口冲击强度 | ISO 179 | 76 | kJ/m2 | ||
| 简支梁缺口冲击强度 | ISO 179 | 无断裂 | |||
| 悬壁梁缺口冲击强度 | 3.20 mm | ASTM D256 | 880 | J/m | |
| 6.40 mm | ASTM D256 | 140 | J/m | ||
| 热性能 | 热变形温度 | 0.45 MPa, 未退火 | ASTM D648 | 142 | ℃ |
| 1.8 MPa, 未退火 | ASTM D648 | 132 | ℃ | ||
| 1.8 MPa, 未退火 | ISO 75-2/A | 129 | ℃ | ||
| 维卡软化温度 | ISO 306/B50 | 149 | ℃ | ||
| 线形膨胀系数 | 流动 | ASTM D696 | 7.0E-5 | cm/cm/℃ | |
| 横向 | ASTM D696 | 7.0E-5 | cm/cm/℃ | ||
| RTI Elec | 1.47 mm | UL 746 | 125 | ℃ | |
| RTI Imp | 1.47 mm | UL 746 | 115 | ℃ | |
| RTI Str | 1.47 mm | UL 746 | 125 | ℃ | |
| 电气性能 | 表面电阻率 | ASTM D257 | 1.0E+15 | ohm | |
| 体积电阻率 | -- | ASTM D257 | 3.0E+18 | ohm·cm | |
| -- | IEC 60093 | 1.0E+15 | ohm·cm | ||
| 介电强度 | 1.60 mm 4 | ASTM D149 | 30 | kV/mm | |
| -- | IEC 60243-1 | 30 | kV/mm | ||
| 介电常数 | 60 Hz | ASTM D150 | 2.95 | ||
| 1 MHz | ASTM D150 | 2.90 | |||
| 100 Hz | IEC 60250 | 3.10 | |||
| 1 MHz | IEC 60250 | 3.00 | |||
| 耗散因数 | 60 Hz | ASTM D150 | 4.0E-4 | ||
| 1 MHz | ASTM D150 | 9.0E-3 | |||
| 100 Hz | IEC 60250 | 1.0E-3 | |||
| 耐电弧性 | ASTM D495 | 110 | sec | ||
| 相比耐漏电起痕指数(CTI) | UL 746 | 300 | V | ||
| 漏电起痕指数 | IEC 60112 | 250 | V | ||
| 可燃性 |
UL 阻燃等级 | 1.90mm | UL 94 | HB | |
| 0.400 mm | UL 94 | V-2 | |||
| 其它性能 | 折射率 | ASTM D542 | 1.585 | ||
| 透射率 | 3000 μm | ASTM D1003 | 88.0 | % | |